Test Data | Guangdong Jingyuan Technology Co., Ltd.

Guangdong Jingyuan Technology Co., Ltd.GUANGDONG JINGYUAN

QUICK CATEGORY SWITCH

Switch related sections without returning home

Test evidence, technical insight and files are organised separately for review and download.

EVIDENCE LEDGER

Conditions before conclusions

Data applies to the stated material, formulation and test conditions and is for selection and pilot-test reference only.

01

TEST RECORD

Flame-retardant Nylon: 5%, 10% and 15%

The source records the stated formulation and comparative results. Values apply only to the listed material and test conditions.

Best in group: 10%
Test date: 2025-07-16
Notched impact: 8.1→11.3 kJ/m²
Tensile strength: 104→125 MPa

02

TEST RECORD

PA6/PA66 with 8% Whisker

The source records the stated formulation and comparative results. Values apply only to the listed material and test conditions.

Test date: 2025-08-25
Suggested dosage: 8%
Notched impact: 9.5→10.2 kJ/m²
Tensile strength: 100→103 MPa

03

TEST RECORD

PA6 Whisker / Glass-fibre Hybrid

The source records the stated formulation and comparative results. Values apply only to the listed material and test conditions.

Hybrid formulation: 15% GF + 15% whisker
Tensile strength: 147 MPa
Flexural strength: 218 MPa
Notched impact: 14 kJ/m²

04

TEST RECORD

PP Fibre and HDPE Product Tests

The source records the stated formulation and comparative results. Values apply only to the listed material and test conditions.

Evaluation focus: modulus, impact, thickness, cost
Material systems: PP / HDPE

05

TEST RECORD

PBAT Biodegradable Film Test

The source records the stated formulation and comparative results. Values apply only to the listed material and test conditions.

Suggested dosage: 30% / 45%
Process: masterbatch / direct film blowing

06

TEST RECORD

Tread Rubber with 10% Whisker

The source records the stated formulation and comparative results. Values apply only to the listed material and test conditions.

Suggested dosage: 10%
Tensile strength: 18.6 vs 17.2 MPa
Abrasion: 183.6 vs 187.3
Elongation at break: 521% vs 499%

07

TEST RECORD

Adhesive and Structural Bonding Tests

The source records the stated formulation and comparative results. Values apply only to the listed material and test conditions.

Material systems: epoxy / SBS / PU / tile adhesive
Surface treatment: KH-550 where stated

APPLICATION DESK

Submit a Request

Crystal-form selection, surface treatment, formulation matching, pilot tests and scale-up support.